| 1. Identificação | |
| Tipo de Referência | Artigo em Evento (Conference Proceedings) |
| Site | plutao.sid.inpe.br |
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
| Identificador | J8LNKAN8RW/36KNJG2 |
| Repositório | dpi.inpe.br/plutao@80/2009/12.22.14.18.36 |
| Última Atualização | 2015:04.01.19.47.20 (UTC) administrator |
| Repositório de Metadados | dpi.inpe.br/plutao@80/2009/12.22.14.18.37 |
| Última Atualização dos Metadados | 2018:06.05.00.12.51 (UTC) administrator |
| Chave Secundária | INPE--PRE/ |
| Rótulo | lattes: 5076862030728693 6 MartinsSiHeBoSoMa:2009:MiEvTi |
| Chave de Citação | MartinsSiHeBoSoMa:2009:MiEvTi |
| Título | Microstructural evolution of Ti-10Nb and Ti-15Nb alloys produced by the blended elemental technique  |
| Formato | DVD |
| Ano | 2009 |
| Data de Acesso | 25 maio 2024 |
| Tipo Secundário | PRE CI |
| Número de Arquivos | 1 |
| Tamanho | 7212 KiB |
| 2. Contextualização | |
| Autor | 1 Martins, Gislene Valdete 2 Silva, Cosme Roberto Moreira da 3 Henriques, Vinicius André Rodrigues 4 Borges Junior, Luiz Antonio 5 Souza, José Vitor Candido de 6 Machado, João Paulo Barros |
| Grupo | 1 LAS-CTE-INPE-MCT-BR 2 3 4 5 LAS-CTE-INPE-MCT-BR 6 LAS-CTE-INPE-MCT-BR |
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Universidade de Brasília (UnB) 3 Instituto de Aeronáutica e Espaço (IAE) 4 UNIFOA 5 Instituto Nacional de Pesquisas Espaciais (INPE) 6 Instituto Nacional de Pesquisas Espaciais (INPE) |
| Endereço de e-Mail do Autor | 1 givmartins@yahoo.com.b 2 cosmeroberto@gmail.com 3 vinicius@iae.cta.br 4 borges.jr@itelefonica.com.br 5 vitor@las.inpe.br 6 joaopaulo@las.inpe.br |
| Endereço de e-Mail | joaopaulo@las.inpe.br |
| Nome do Evento | International Latin American Conference on Powder Technology, 17. |
| Localização do Evento | Atibaia, SP |
| Data | 8-10 Nov. |
| Volume | 1 |
| Título do Livro | Proceedings |
| Tipo Terciário | Paper |
| Histórico (UTC) | 2009-12-23 14:00:41 :: lattes -> marciana :: 2010-01-19 10:42:37 :: marciana -> administrator :: 2018-06-05 00:12:51 :: administrator -> marciana :: 2009 |
| 3. Conteúdo e estrutura | |
| É a matriz ou uma cópia? | é a matriz |
| Estágio do Conteúdo | concluido |
| Transferível | 1 |
| Tipo do Conteúdo | External Contribution |
| Tipo de Versão | publisher |
| Palavras-Chave | Ti-Nb alloy powder metallurgy microstructure and mechanical properties |
| Resumo | Alfa/beta titanium alloys have been intensely used for aerospace and biomedical applications. Production of powder metallurgy titanium alloys components may lead to a reduction in the cost of parts, compared to those produced by conventional cast and wrought (ingot metallurgy) processes, because additional working operations (machining, turning, milling, etc.) and material waste can be avoided. In this work, samples of Ti- 10, 15Nb (weight%) alloys were obtained by the blended elemental technique using hydride-dehydride (HDH) powders as raw material, followed by uniaxial and cold isostatic pressing with subsequent densification by sintering carried out in the range 9001500 ºC. These alloys were characterized by X-ray diffractometry for phase composition, scanning electron microscopy for microstructure, Vickers indentation for hardness, Archimedes method for specific mass and resonance ultrasound device for elastic modulus. For the samples sintered at 1500ºC it was identified α and β phases. It was observed the influence of the sintering temperatures on the final microstructure. With increasing sintering temperature, microstructure homogenization of the alloy takes place and at 1500 ºC this process is complete. The same behavior is observed for densification. Comparing to the Ti6Al4V alloy properties, these alloys hardness (sintered at 1500 ºC) are near and elastic modulus are 18% less. |
| Área | FISMAT |
| Arranjo | Fonds > Produção anterior à 2021 > LABAS > Microstructural evolution of... |
| Conteúdo da Pasta doc | acessar |
| Conteúdo da Pasta source | não têm arquivos |
| Conteúdo da Pasta agreement | não têm arquivos |
| 4. Condições de acesso e uso | |
| URL dos dados | http://plutao.sid.inpe.br/ibi/J8LNKAN8RW/36KNJG2 |
| URL dos dados zipados | http://plutao.sid.inpe.br/zip/J8LNKAN8RW/36KNJG2 |
| Idioma | en |
| Arquivo Alvo | martins_microstructural.pdf |
| Grupo de Usuários | lattes marciana administrator marciana |
| Grupo de Leitores | administrator marciana |
| Visibilidade | shown |
| Permissão de Leitura | allow from all |
| Permissão de Atualização | não transferida |
| 5. Fontes relacionadas | |
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 |
| Acervo Hospedeiro | dpi.inpe.br/plutao@80/2008/08.19.15.01 |
| 6. Notas | |
| Campos Vazios | archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel dissemination doi edition editor isbn issn lineage mark mirrorrepository nextedition notes numberofvolumes orcid organization pages parameterlist parentrepositories previousedition previouslowerunit progress project publisher publisheraddress resumeid rightsholder schedulinginformation secondarydate secondarymark serieseditor session shorttitle sponsor subject tertiarymark type url |
| 7. Controle da descrição | |
| e-Mail (login) | marciana |
| atualizar | |